FusRock

FusRock PETG-CF Filament

$38.95 Sold out
Tax included. Shipping calculated at checkout.
Apply

Pickup availability at Regents Park Warehouse/Service Center

Out of stock.

Pickup Availability
  • Regents Park Warehouse/Service Center
    Out of stock.

    6 Rose Crescent
    Regents Park NSW 2143
    Australia

    (02) 9772 4315

Shipping & Returns
  • One Year National Warranty
  • Support by Bambu LabAuthorised Service Center
  • Free Shipping over $150. (excluded 3d printer & AMS)

Β 

FusFunβ„’Β PETG-CF is a PETGΒ basedΒ withΒ choppedΒ carbonΒ fiberΒ reinforcedΒ FFF material that improves warping resistance, reduces size shrinkage during printing and improves overhang surface quality while giving the material a frosted surface texture.

Β 

Material Properties

PropertyTesting methodTypical value
Density ISO 1183 1.23 g/cmΒ³
Glass transition temperature ISO 11357 78℃
Melt index 230β„ƒοΌŒ2.16kg 4.5g/10min
Determination of temperature ISO 75: Method A 74℃ (1.8MPa)
Determination of temperature ISO 75: Method B 77℃ (0.45MPa)
Tensile strength(X-Y) ISO 527 46.11Β±0.75 MPa
Elongation at Yield ISO 527 3.56Β±0.05%
Young's Modulus ISO 527 2616Β±25MPa
Tensile breaking strength ISO 527 41.70Β±0.98 MPa
Elongation at break ISO 527 5.53Β±0.22%
Tensile breaking strength （ZοΌ‰ ISO 527 25.1Β±1.9MPa
Elongation at break (Z) ISO 527 1.81Β±0.3%
Young’s modulus (Z) ISO 527 1856Β±41MP
Elongation at break (Z) ISO 527 1.55 Β± 0.12 %
Bending strength (X-Y) ISO 178 66.80Β±1.32MPa
Bending Modulus (X-Y) ISO 178 2291Β±42MPa
Charpy impact strength (X-Y) ISO 179 5.11±1.01 KJ/㎑

Specimens printed under the following conditions: Nozzle size 0.4mm，Nozzle temp 250°C, Bed temp 75°C, Print speed 40mm/s, Infill 100%, Infill angle ±45°

Β 

Β 

Recommended printing conditions

Nozzle Temperature240-260Β°C
Recommended Nozzle Diameter 0.4-1.0mm
Recommended build surface treatment Glass、PEI Film or Coating with PVP glue
Build plate temperature 70-80 Β°C
Raft separation distance 0.2-0.25mm
Cooling fan speed ≀50%
Print speed 30-60 mm/s
Retraction distance 2-5 mm
Retraction speed 1800-2400 mm/min

Printing Tips： 1、The wear resistance of copper nozzle is poor. It is recommended to use stainless steel or hardened steel nozzle to print, which can effectively improve the printing quality. 2、Please put filament into a dry box, which can effectively reduce the oozing, rough surface and so on.