FusRock FusForce™ PAHT-CF
From $66.99 Select options

FusRock FusForce™ PAHT-CF

From $66.99

* Get free shipping for orders over $150.00

FusRock FusForce™ PAHT-CF Filament 15% Carbon Fiber Reinforced High-Temperature Polyamide Industrial FDM Materials, high heat resistance.

Local Pickup available at 3D BRO

Usually ready within 15 mins

View store information

FusRock FusForce™ PAHT-CF Filament 1.75mm 0.5/1kg/2.5kg

Formoly FusRock UltraPA CF

High temperature Polyamide based with 15% chopped carbon fiber reinforced FDM material.

User Manual: https://github.com/3dbro-au/FusRock-Filaments/blob/main/FusForce%E2%84%A2%20UltraPA-CF_TDS(EN).pdf 

Product Description

FusForce™ UltraPA CF Filament is specially developed for FDM 3D printing process, and its substrate material is high temperature nylon, which has low density, low moisture absorption, high strength, high abrasion resistance, excellent chemical resistance and high heat resistance

It also has good dimensional stabelity,no warpage and no shrinkage during the printing process, and can be used with FusFree™ S-Purple Quick-Remove Support material to solve the problem of poor molding effect on the support surface of complex models

 

Material Properties

PropertyTesting methodTypical value
DensityISO 11831.15 g/cm³
Water absorptionISO 62: Method 10.60%
Melting TemperatureISO 11357231℃
Melting index280℃, 2.16kg10.78
Determination of temperatureISO 75: Method A113℃ (1.8MPa)
ISO 75: Method B188℃ (0.45MPa)
Tensile strength(X-Y)ISO 527121.77±4.28 Mpa
Toung’s modulus(X-Y)ISO 5277807.99±517.99 Mpa
Elongation at break(X-Y)ISO 5271.88±0.11%
Bending strength (X-Y)ISO 178190.85±2.07 Mpa
Bending modulus (X-Y)ISO 1788512.22±241.31 Mpa
Charpy impact strength (X-Y)ISO 1797.74±1.13 KJ/m³
Single Shell Z-axis tensile strengthCustom method: Vase mode41.90±3.87 Mpa
Nozzle size 0.6mm/Layer height 0.3mm
Layer time 20s

Recommanded Printing conditions

Nozzle Temperature300-320℃
Recommanded Nozzle Diameter0.4-1.0mm
Recommanded build surface treatmentPEI film or Coating with PVP glue
Build plate temperature70-80℃
Raft separation distance0.12-0.16mm
Cooling fan speedoff
Print speed30-60mm/s
Retraction distance3-6mm
Retraction speed1800-3600mm/min

 

 

Recommended Nozzle:

  1. Hardened Steel Nozzle 1100-HS
  2. DLC Hardened Steel Nozzle 1100-HSD
  3. Ruby Nozzle A019
  4. Tungsten Carbide Nozzle

 

Recommended Hotend:

  1. Dragon series
  2. Dragonfly series

 

Product Advantages

Smart Fiber Reinforced Technology

FusRock controlling the dispersion and distribution of chopped carbon fibers within the material matrix during the extrusion process, the fibers form a mesh skeleton structure within the material and bear most of the load transferred by the material matrix. Smart Fiber Reinforced Technology greatly improves the mechanical properties and heat resistance of the material, and releases the internal stress during the printing process through the fiber mesh structure, resulting in good dimensional stability of the printed part and no warpage.

 

Low Mositure Sensitivity

FusForce™ UltraPA-CF based on modified PA12 long-chain nylon, whose saturated moisture absorption rate is only one tenth of ordinary PA6, completely solving the defects of the mechanical properties and dimensional stability of nylon materials that change greatly after absorbed moisture.

 

Super Abrasive Resistance

FusForce™ UltraPA-CF has a low coefficient of friction, self-lubricating properties and excellent wear resistance, which can easily meet all kinds of high-strength gears or industrial applications with high wear requirements.

 

Specimens printed under the following conditions: Nozzle temp 320°C, Bed temp 80°C, Print speed 45mm/s, ln’ill 100%, Infill angle±45°, Post-processing: 100°C Annealing 8 hours

 

 

Additional Suggestions:

1. Nylon material is very easy to absorb moisture within the environment, and printing after absorbing moisture will result ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the FusForce  UltraPA-CF vacuum foil bag for printing Please put the unused filament back into the original aluminum foil bag for sealed storage

 

2. After the material is damp, there will be more printing ozzing, bubbles extruded and rough printing surface. Please dry the filament in an oven at 80-100°C for 4-6h to restore the printing quality of FusForce  UltraPA-CF

 

3. It is recommended to use hardened steel and above grade nozzles made by Phaetus, which can effectively improve the print quality. Besides, it is recommended that the thickness of the heating block is longer 12mm

 

4. After the printing is completed, the printed part can be annealed to further improve the strength of print part. Annealing conditions: leave printing part in an oven at 80-100°C for 4 to 8 hours and cool to room temperature naturally

 